Home>Products> rubber fiber gasket > Non-asbestos Rubber Gasket

Synthetic Fiber Gasket

Model NO.: NY4250 Gasket
Type: Oil Seal
Performance: Temperature
Shape: O-Ring
Standard: Standard
Certificate: ISO9001

Send Inquiry

Description

Basic Info.

Model NO.	NY4250 Blue Gasket
Type	Oil Seal
Performance	Temperature
Shape	Multihole O-Ring
Standard	Standard
Certificate	ISO9001
Applicable Medium	Oil Resistance, Water Resistance, General Acid
Main Material	Fiber, NBR
Usage	Shipbuilding, pump valve, plumbing and sanitary ware, pipe valve, mechanical assembly, etc.
Temperature Range	-50-300ºC
Transport Package	Wooden Box
Specification	customizable
Trademark	BTT
Origin	China
Production Capacity	1200000PCS/Year

Packaging & Delivery

Package Size	800800400MM
Package Gross Weight	300.000kg

Product Description

Product introduction

Dive into the superior quality of our innovative product crafted from the finest non-metallic materials. With nitrile rubber as its binder and a robust blend of organic and inorganic fibers as its framework, this eco-friendly sealing plate is precision-formed through advanced roller pressing. Its remarkable resistance to oil, water, and common acids and alkalis ensures unparalleled performance. Engineered to operate efficiently in a wide temperature range from -50 to 300ºC, this product is a testament to sophisticated sealing technology.

Specifications: Lovingly customizable to your exact needs.
Main thickness: Elegantly ranging from 0.4-10.0MM
Main colors: Available in a stunning palette of blue, green, and black.
The product boasts a thickness greater than 1.0mm and can be enhanced with a clip-on steel wire for added durability.

Performance introduction

Number	Test item	Unit	Parameter value
1	Density, ASTMF-1315	G/cm³	1.9±0.1
2	Strength, ASTMF-152	Mpa	≥7.0
3	Compression, ASTMF-36	%	7-17
4	Resilient rate, ASTMF-36	%	≥40
5	Sealing, ASTMF-37	Ml/min	≤1.0
Note 1: The gasket material with thickness greater than 3.0mm shall not be tested for transverse tensile strength Note 2: screen reinforced gasket material, do not do transverse tensile strength and nitrogen leakage rate test Note 3:The temperature test was GB/T540-2008 heat and pressure resistance test, the experimental conditions were 300℃ temperature, 8mpa steam pressure, maintained for 30min, no breakdown.